Product Information - PLANTIC™ RV Rigid VSP
PLANTIC™ RV is a PET high barrier thermoformable packaging material that enables the functionality of a Polyethylene seal, extending shelf life, whilst retaining the recyclability of the total pack.
Recyclable, High Barrier packaging material for Thermoforming
Made from high amylose starch, a renewable resource that will lower your packaging greenhouse gas emissions.
Kerbside recyclable barrier packaging. Maintain Colour branding as the Colour is added to the dissolvable barrier PLANTIC™ layer.
Thermoformable PET rigid roll stock or tray in bespoken sizes and thickness with low sealing temperatures anti-static properties.
Ultra-low Gas Barrier Transmission providing extended shelf life to reduce product waste with Peelable/Lock seal capability.
APPLICATIONS
PLANTIC™ RV is versatile in application and suitable to most Vacuum Skin Pack Packaging (VSP) applications. The sealant layer is compatible with most available VSP top webs using a PE sealant layer.
QUALITY
Plantic manufacturing location in Australia is accredited to Food Safety System Certification 22000 (FSSC 22000).
FOOD COMPLIANCE APPROVAL.
This product meets the requirements of Federal Food, Drug and Cosmetics Act. This includes Food Types, as defined in 21CFR176.170(c), III, IVA, V, VIIA, VIII and IX for conditions of use E through G.
PRODUCT CHARACTERISTICS
| Thickness Range | 250µm to 700µm (+/- 5%) * |
| Roll Width Range | 250-1000mm (+/- 1mm) * |
*For any other thickness, width, or Colour requirements, please contact Plantic Technologies Ltd.
TECHNICAL DATA
Barrier Properties
| Property | Test Method | Value | Units |
|---|---|---|---|
| Water Vapour Transmission Rate | ASTM F1249-01 | <3* | g/m2/24h @ 38°C and 90%RH |
| Oxygen Transmission Rate | ASTM F1927-98 | <0.5* | cm3/m2/24h @ 23°C, 50%RH |
* Test results for 450µm PLANTIC™ RV.
* Correlation of measured values should be validated with actual shelf-life analysis.
Physical properties Test results for 450µm PLANTIC™ RV
| Property | Test Method | Value | Units |
|---|---|---|---|
| Density | ASTM D792 | 1.33 | g/cm3 (23°C and 50%RH) |
| Yield (Nominal) | ASTM D4321 | 1.72 | m2/kg (23°C and 50%RH) |
| Tensile Modulus | ASTM D882 | 1709 | MPa (23°C and 50%RH) |
| Tensile Strength | ASTM D882 | 8.34 | MPa (23°C and 50%RH) |
| Elongation at break | ASTM D882 | 176 | % (23°C and 50%RH) |
| Impact Strength | ASTM D3420 | 33 | mN/mm (23°C and 50%RH) |
| Seal Strength | Commercial | >12-20 | N/15mm |
Thermal Properties
| Property | Value | Units |
|---|---|---|
| Sealing temperature | 150-200* | °C |
| Thermoforming temperatures | 90-110** | °C |
*Sealing is achieved with compatible PE top lid films. For more seal condition guidelines, please contact Plantic Technologies Ltd.
**For more information on thermoforming conditions (heating and forming time, pressures etc....) please contact
End of Life Properties
| Property | Comment |
|---|---|
| GHGs | 50% less than conventional PET barrier & non barrier |
| Recyclability Status* | Kerbside recyclable |
*Subject to evolving country’s standards.
OTR Modelling and Validation
A simulation model is used to predict the time‑dependent (transient) oxygen transmission rate (OTR) of the multilayer structures. The model is based on the measured oxygen permeability and diffusivity of the individual skin and barrier layers.
The predicted OTR closely matches the values measured experimentally using a Mocon OTR system. This strong agreement confirms that the observed transient OTR behavior is primarily driven by the high moisture content of the Plantic barrier layer and the diffusion characteristics of Plantic.